| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 熔流率 | ASTM D1238 | 2.1 | g/10 min | |
| 醋酸乙烯含量 | 190°C/2.16 kg) | ExxonMobil Method | 9.4 | wt% | |
| 支撐硬度 | 支撐 A, 15 秒 | ISO 868 | 93 | ||
| 机械性能 | 拉伸模量 | ISO 527-2 | 90.0 | MPa | |
| 割线模量 | 1% 正割, MD | ASTM D882 | 90.0 | MPa | |
1% 正割, TD | ASTM D882 | 95.0 | MPa | ||
| 抗张强度 | MD: 断裂 | ASTM D882 | 28.0 | MPa | |
TD: 断裂 | ASTM D882 | 27.0 | MPa | ||
| 伸长率 | MD: 断裂 | ASTM D882 | 550 | % | |
TD: 断裂 | ASTM D882 | 650 | % | ||
| 落锤冲击 | ASTM D1709A | 390 | g | ||
| 埃尔曼多夫抗撕强度 | MD | ASTM D1922 | 120 | g | |
TD | ASTM D1922 | 190 | g | ||
| 热性能 | 维卡软化温度 | ASTM D1525 | 78.5 | °C | |