| 厂家(产地) | 美国杜邦 |
|---|---|
| 牌号 | 7130l |
| 加工级别 | 注塑级 |
| 特性级别 | 阻燃级,增强级,透明级,耐高温 |
| 销售方式 | 品牌经销 |
| 类型 | 标准料 |
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | 黑色 | ASTM D-792 | 1.62 | |
| 模缩率 | 流向1.6mm | ASTM D-955 | -0.1 | % | |
| 泰伯摩擦 | ASTM D-1044 | 63 | mg | ||
| 模缩率 | 流向3.2mm | ASTM D-955 | 0 | % | |
| 模缩率 | 横向1.6mm | ASTM D-955 | 0.9 | % | |
| 机械性能 | 弯曲模量 | 23℃,1.6mm | ASTM D-790 | 14000 | MPa |
| 无缺口冲击强度 | 23℃,3.2mm | ASTM D-4812 | 555,20%NB | j/m | |
| 弯曲模量 | 23℃,0.8mm | ASTM D-790 | 18000 | MPa | |
| 冲击下机械性能 | UL 746B | 210 | ?C | ||
| 拉伸模量 | 23℃,3.2mm | ASTM D-638 | 18000 | MPa | |
| 弯曲模量 | 23℃,3.2mm | ASTM D-790 | 13100 | MPa | |
| 拉伸强度 | 23℃,1.6mm | ASTM D-638 | 173 | MPa | |
| IZOD冲击强度 | 23℃,0.8mm | ASTM D-256 | 400,40%NB | j/m | |
| 无缺口冲击强度 | 23℃,1.6mm | ASTM D-4812 | 840 | j/m | |
| 模缩率 | 横向3.2mm | ASTM D-955 | 0.8 | % | |
| 弯曲强度 | 23℃,3.2mm | ASTM D-790 | 183 | MPa | |
| 弯曲强度 | 23℃,0.8mm | ASTM D-790 | 215 | MPa | |
| 压缩强度 | 3.2mm | ASTM D-695 | 89 | MPa | |
| 拉伸模量 | 23℃,1.6mm | ASTM D-638 | 19306 | MPa | |
| 断裂伸长率 | 23℃,3.2mm | ASTM D-638 | 1.7 | % | |
| 弯曲疲劳 | 3.2mm，69MPa | ASTM D-671 | 2667 | cycle | |
| 断裂伸长率 | 23℃,1.6mm | ASTM D-638 | 1.6 | % | |
| IZOD冲击强度 | 23℃,3.2mm | ASTM D-256 | 225 | j/m | |
| 洛氏硬度 | Scale M | ASTM D-785 | 63 | ||
| 拉伸强度 | 23℃,3.2mm | ASTM D-638 | 150 | MPa | |
| 弯曲强度 | 23℃,1.6mm | ASTM D-790 | 192 | MPa | |
| IZOD冲击强度 | 23℃,1.6mm | ASTM D-256 | 170 | j/m | |
| 电气性能 | 介电强度 | 1.6mm逐步 | ASTM D-149 | 31 | KV/mm |
| 介电常数 | 23℃,0.8mm,1×109Hz | ASTM D-2520B | 4.4 | ||
| 介电常数 | 23℃,3.2mm,1×103Hz | ASTM D-150 | 4.3 | ||
| 损耗因素 | 23℃,1.6mm,1×109Hz | ASTM D-2520B | 0.004 | ||
| 损耗因素 | 23℃,3.2mm,1×106Hz | ASTM D-150 | 0.029 | ||
| 损耗因素 | 23℃,3.2mm,1×109Hz | ASTM D-2520B | 0.004 | ||
| 介电强度 | 23℃,1.6mm短时间 | ASTM D-149 | 35 | KV/mm | |
| 介电强度 | 23℃,3.2mm短时间 | ASTM D-149 | ＞28 | KV/mm | |
| 介电常数 | 23℃,3.2mm,1×106Hz | ASTM D-150 | 3.8 | ||
| 体积电阻率 | ASTM D-257 | 1×1016 | Ω.cm | ||
| 损耗因素 | 23℃,3.2mm,1×103Hz | ASTM D-150 | 0.013 | ||
| 介电常数 | 23℃,3.2mm,1×109Hz | ASTM D-2520B | 4.3 | ||
| 介电常数 | 23℃,0.8mm,1×103Hz | ASTM D-150 | 3.9 | ||
| 损耗因素 | 23℃,0.8mm,1×103Hz | ASTM D-150 | 0.013 | ||
| 损耗因素 | 23℃,0.8mm,1×106Hz | ASTM D-150 | 0.029 | ||
| 损耗因素 | 23℃,0.8mm,1×109Hz | ASTM D-2520B | 0.004 | ||
| 表面电阻率 | ASTM D-257 | 1×1015 | Ω | ||
| 介电常数 | 23℃,0.8mm,1×106Hz | ASTM D-150 | 3.5 | ||
| 加工性能 | 熔解温度范围 | ℃ | 363～371 | ||
| 模具温度范围 | ℃ | 30～95 | |||
| 干燥时间（除湿干燥剂） | 2 | h | |||
| 加工时水气含量 | ＜0.01 | % | |||
| 干燥温度 | 135 | ℃ | |||
| 热性能 | 熔点 | ASTM D-3418 | 352 | ?C | |
| 导热性 | ASTM C-177 | 0.32 | W/m k | ||
| 玻璃转变温度 | ASTM D-3418 | 120 | ?C | ||
| 热变形温度 | ASTM D-648 | 289 | ?C | ||
| 相关温度指数 | UL 746B | 240 | ?C | ||
| 外推**终融温 | ASTM D-3418 | 360 | ?C | ||
| 其它性能 | 厚度测试 | UL 94 | 0.75 | mm | |
| 厚度比率 | UL 94 | V-0 | |||
| 限制氧气指数 | 3.2mm | ASTM D-2863 | 39 | % | |