| 厂家(产地) | 沙特巴塞尔 |
|---|---|
| 牌号 | HP500N |
| 加工级别 | 注塑级 |
| 特性级别 | 高刚性,高流动 |
| 用途级别 | 通用级 |
| 销售方式 | 品牌经销 |
| 类型 | 标准料 |
| Typical Properties | Method | Value | Unit |
| Physical | |||
| Density | ISO 1183 | 0.9 | g/cm? |
| Melt flow rate (MFR) (230°C/2.16kg) | ISO 1133 | 12 | g/10 min |
| Melt volume flow rate (230°C/2.16kg) | ISO 1133 | 16 | cm?/10min |
| Mechanical | |||
| Tensile Modulus | ISO 527-1, -2 | 1550 | MPa |
| Tensile Stress at Yield | ISO 527-1, -2 | 35 | MPa |
| Tensile Strain at Break | ISO 527-1, -2 | >50 | % |
| Tensile Strain at Yield | ISO 527-1, -2 | 10 | % |
| Impact | |||
| Charpy unnotched impact strength | ISO 179 | ||
| (23 °C, Type 1, Edgewise) | 110 | kJ/m? | |
| (0 °C, Type 1, Edgewise) | 30 | kJ/m? | |
| Charpy notched impact strength (23 °C, Type 1, Edgewise, Notch A) | ISO 179 | 3 | kJ/m? |
| Thermal | |||
| Heat deflection temperature B (0.45 MPa) Unannealed | ISO 75B-1, -2 | 95 | °C |
| Vicat softening temperature A/50 | ISO 306 | 153 | °C |
| Vicat softening temperature B/50 | ISO 306 | 85 | °C |
聚丙烯，是由丙烯聚合而制得的一种热塑性树脂。按甲基排列位置分为等规聚丙烯（isotactic polyprolene）、无规聚丙（atacticpolypropylene）和间规聚丙烯（syndiotactic polypropylene）三种。甲基排列在分子主链的同一侧称等规聚丙烯，若甲基无秩序的排列在分子主链的两侧称无规聚丙烯，当甲基交替排列在分子主链的两侧称间规聚丙烯。一般工业生产的聚丙烯树脂中，等规结构含量约为95%，其余为无规或间规聚丙烯。
工业产品以等规物为主要成分。聚丙烯也包括丙烯与少量乙烯的共聚物在内。通常为半透明无色固体，无臭无毒。由于结构规整而高度结晶化，故熔点可高达167℃。耐热、耐腐蚀，制品可用蒸汽消毒是其突出优点。密度小，是**的通用塑料。缺点是耐低温冲击性差，较易老化，但可分别通过改性予以克服。
共聚物型的PP材料有较低的热变形温度（100℃）、低透明度、低光泽度、低刚性，但是有更强的抗冲击强度，PP的冲击强度随着乙烯含量的增加而增大。PP的维卡软化温度为150℃。由于结晶度较高，这种材料的表面刚度和抗划痕特性很好。PP不存在环境应力开裂问题。
PP的熔体质量流动速率（MFR）通常在1~100。低MFR的PP材料抗冲击特性较好但延展强度较低。对于相同MFR的材料，共聚型的抗冲强度比均聚型的要高。由于结晶，PP的收缩率相当高，一般为1.6~2.0%。