| 类型 | 标准料 |
|---|---|
| 密度 | 1.19 |
| 牌号 | 8H |
| 销售方式 | 品牌经销 |
| 颜色 | 本色 |
| 用途级别 | 板材级,型材 |
| 品牌 | 赢创德固赛 |
| 厂家(产地) | 德国 |
| 加工级别 | 挤出级 |
| 特性级别 | 标准级,透明级,高抗冲 |
| 规格级别 | 透明 |
PLEXIGLAS? 8H is an amorphous thermoplastic molding compound (PMMA).
Typical properties of PLEXIGLAS? molding compounds are:
good flow high mechanical strength, surface hardness and mar resistance high light transmission very good weather resistance free colorability due to crystal clarity.
Special properties of PLEXIGLAS? 8H molding compound are:
optimum mechanical properties increased heat deflection temperature high melt strength AMECA listing.
Application:
Used for extruding optical and technical profiles and sheets.
Examples:
sheets, tubes, multi-skin sheets, coextrusion of window profiles and similar applications
Processing:
PLEXIGLAS? 8H can be processed on extruders with 3-zone general purpose screws for engineering thermoplastics.
Physical Form / Packaging:
PLEXIGLAS? molding compounds are supplied as pellets of uniform size, packaged in 25kg polyethylene bags or in 500kg boxes with PE lining; other packaging on request. Plexiglas? 8H 物性表
| 基本信息 | |
|---|---|
| 黄卡编号 | E65495-247805 |
| 特性 | 高 ESCR（抗应力开裂） 良好的流动性 良好的熔体强度 良好的着色性 耐气候影响性能良好 硬度高 |
| 用途 | 管件 门窗 片材 型材 |
| 形式 | 粒子 |
| 加工方法 | 共挤出成型 挤出 |
| 多点数据 | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2) |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.19 | g/cm3 | ISO 1183 |
| 溶化体积流率（MVR） (230°C/3.8 kg) | 0.800 | cm3/10min | ISO 1133 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 3300 | MPa | ISO 527-2/1 |
| 拉伸应力 (断裂) | 78.0 | MPa | ISO 527-2/5 |
| 拉伸应变 (断裂) | 6.5 | % | ISO 527-2/5 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁无缺口冲击强度 (23°C) | 20 | kJ/m2 | ISO 179/1eU |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | 108 | °C | ISO 306/B50 |
| 线形热膨胀系数 - 流动 (0 到 50°C) | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| 可燃性 | 额定值 | 测试方法 | |
|---|---|---|---|
| UL 阻燃等级 (1.60 mm) | HB | UL 94 | |
| Fire Rating | B2 | DIN 4102 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 折射率 | 1.490 | ISO 489 | |
| 透射率 1 | 92.0 | % | ISO 13468-2 |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | < 98.0 | °C | |
| 干燥时间 | 2.0 到 3.0 | hr | |
| 熔体温度 | 220 到 260 | °C | |
| 口模温度 | 220 到 260 | °C |