| 产品说明 | |
| PRIMACOR™ 3004 is an ethylene acrylic acid copolymer designed for extrusion/coextrusion coating and laminating. It provides excellent hot tack and adhesion to metallic, paper and polyethylene substrates with excellent heat seal strength, even through many oil and powdered products. This resin also offers outstanding resistance to delamination, as well as excellent toughness and environmental stress crack resistance (ESCR). Excellent draw down and edge stabilityExcellent product resistanceExcellent hot tack, heat seal, toughnessHigh performance sealant or tie layer Complies with: U.S. FDA 21 CFR 177.1310(b)EU, No 10/2011Consult the regulations for complete details. | |
| 形式 | 颗粒料 |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 比重 | 0.938 | g/cm³ | ASTM D792, ISO 1183 |
| 熔流率 2 (190°C/2.16 kg) | 8.5 | g/10 min | ASTM D1238, ISO 1133 |
| 共聚单体含量 3 | 9.7 | % |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 抗张强度 | ASTM D638, ISO 527-2 | ||
| 屈服, 模压成型 | 7.93 | MPa | |
| 断裂, 模压成型 | 17.6 | MPa | |
| 伸长率 (断裂, 模压成型) | 600 | % | ASTM D638, ISO 527-2 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 维卡软化温度 | 81.1 | °C | ASTM D1525, ISO 306 |
| 溶融温度（DSC） | 98.0 | °C | Internal Method |
| 挤出 | 额定值 | 单位制 | 测试方法 |
| 熔体温度 | 260 到 290 | °C | |
| 内缩量 (288°C, 25.4 µm) | 50.8 | mm | Internal Method |
| **小涂层厚度 | 10 | µm | Internal Method |
| **小涂层重量 | 9.8 | g/m² | Internal Method |
| 挤压说明 | |||
| 挤出涂层薄膜的制造条件： 用于处理此树脂的设备应由耐腐蚀材料制成。建议模具和适配器采用不锈钢和/或双面镀铬或镀镍。 螺杆尺寸：3.5 英寸 (89 mm)；30:1 L/D模具：30 英寸模具切边至 24 英寸模具间隙：20 密尔 (0.508 mm)熔体温度：550°F (288°C)输出：250 磅/小时气隙：6 英寸 (152 mm) | |||