东莞市东如信塑胶原料有限公司长期供应SABIC（沙伯基础创新塑料） GELOY ASA，ASA/PC，长期供应，柜货订购，原厂原装，可开税票，可送货上门，可到仓库看货，可提供材质报告，物性表、MSDS、REACH、SGS、 出厂证明，外加技术指引等，欢迎来电洽谈，电话：15818367582/18938556268，刘先生
| TYPICAL PROPERTIES(1) |
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 420 | kgf/cm? | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 350 | kgf/cm? | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 40 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 18200 | kgf/cm? | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 590 | kgf/cm? | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 18200 | kgf/cm? | ASTM D 790 |
| Hardness, Rockwell R | 86 | - | ASTM D 785 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 32 | cm-kgf/cm | ASTM D 256 |
| Izod Impact, notched, -30°C | 5 | cm-kgf/cm | ASTM D 256 |
| Gardner Impact (Procedure B) | 1088 | cm-kgf/cm | ASTM D 4226 |
| Instrumented Impact Total Energy, 23°C | 259 | cm-kgf | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 99 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 87 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 76 | °C | ASTM D 648 |
| HDT, 1.82 MPa, annealed | 95 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 90 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 79 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 8.64E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 9.18E-05 | 1/°C | ASTM E 831 |
| CTE, -30°C to 0°C, flow | 8.46E-05 | 1/°C | ASTM E 831 |
| CTE, 0°C to 100°C, flow | 9.E-05 | 1/°C | ASTM E 831 |
| Relative Temp Index, Elec | 50 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 50 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 50 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.06 | - | ASTM D 792 |
| Water Absorption, equilibrium, 23C | 0.55 | % | ASTM D 570 |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.5 - 0.7 | % | SABIC Method |
| Melt Flow Rate, 220°C/10.0 kgf | 7 | g/10 min | ASTM D 1238 |
| Melt Flow Rate, 260°C/5.0 kgf | 13 | g/10 min | ASTM D 1238 |
| OPTICAL | Value | Unit | Standard |
| Gloss, untextured, 60 degrees | 95 | - | ASTM D 523 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | >1.E+15 | Ohm | ASTM D 257 |
| Dielectric Strength, in oil, 3.2 mm | 15.9 | kV/mm | ASTM D 149 |
| Relative Permittivity, 50/60 Hz | 5.2 | - | ASTM D 150 |
| Relative Permittivity, 1 MHz | 3.21 | - | ASTM D 150 |
| Dissipation Factor, 50/60 Hz | 0.15 | - | ASTM D 150 |
| Dissipation Factor, 1 MHz | 0.026 | - | ASTM D 150 |
| Hot Wire Ignition {PLC) | 3 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94HB Flame Class Rating (3) | 1.49 | mm | UL 94 |
| UV-light, water exposure/immersion | F2 | - | UL 746C |
13861291831