| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 熔体流动速率 | 220℃/10kg | ASTM D-1238 | 60 | g/10min |
| 比重 | ASTM D-792 | 1.19 | ||
| 成型收缩率 | ASTM D-955 | 0.004-0.007 | mm/mm | |
| 弯曲弹性率 | ASTM D-790 | 710 | kg/cm2 | |
| 冲击强度 | Notched1/4" | ASTM D-256 | 19 | kgcm/cm |
| 洛氏硬度 | ASTM D-785 | 102 | R-Scale | |
| 延伸率 | ASTM D-638 | 18 | % | |
| 挠曲模量 | ASTM D-790 | 24000 | kg/cm2 | |
| 拉伸强度 | ASTM D-638 | 430 | kg/cm2 | |
| HVTR | UL-746A | 1 | PLCCod | |
| HWI | UL-746A | 4 | PLCCode | |
| 抗弧光 | ASTM D-495 | 6 | PLCCode | |
| HAI | UL-746A | 0 | PLCCode | |
| CTI | UL-746A | 2 | PLCCode | |
| 维卡软化点 | 1.000g | ASTM D-1525 | 85 | ℃ |
| 热变形温度 | Unannealed18.5kg/cm1/2" | ASTM D-648 | 76 | ℃ |
| 燃烧率 | 1/8" | UL-94 | V-0 | |
| 燃烧率 | 1/16" | IEC-707 | FV-0 | mm/min |
| 燃烧率 | 1/16" | UL-94 | V-0 |