LG ABS AF312C 物性表
基本信息
| 黄卡编号 | |
| 特性 |
|
| 用途 |
|
| 加工方法 |
|
| 比重 | 1.18 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (220°C/10.0 kg) | 58 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 (3.20 mm) | 0.40 到 0.70 | % | ASTM D955 |
| 洛氏硬度 (R 级) | 104 | ASTM D785 |
| 拉伸模量 1(3.20 mm) | 2160 | MPa | ASTM D638 |
| 抗张强度 2(屈服, 3.20 mm) | 45.1 | MPa | ASTM D638 |
| 伸长率 3 | ASTM D638 | ||
| 屈服, 3.20 mm | 5.0 | % | ASTM D638 |
| 断裂, 3.20 mm | 20 | % | ASTM D638 |
| 弯曲模量 4(6.40 mm) | 2550 | MPa | ASTM D790 |
| 弯曲强度 5(屈服, 6.40 mm) | 68.6 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 | ASTM D256 | ||
| -30°C, 3.20 mm | 78 | J/m | ASTM D256 |
| -30°C, 6.40 mm | 78 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 260 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 230 | J/m | ASTM D256 |
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 6.40 mm 6 | 84.0 | °C | ASTM D648 |
| 0.45 MPa, 未退火, 6.40 mm 7 | 76.0 | °C | ASTM D648 |
| 维卡软化温度 | 84.0 | °C | ASTM D1525 8 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 70.0 | °C | UL 746 |
| RTI | 80.0 | °C | UL 746 |
| UL 阻燃等级 | UL 94 | ||
| 2.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| 干燥温度 | 70.0 到 80.0 | °C | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 建议的最大水分含量 | < 0.010 | % | |
| 料筒后部温度 | 170 到 190 | °C | |
| 料筒中部温度 | 180 到 200 | °C | |
| 料筒前部温度 | 190 到 210 | °C | |
| 射嘴温度 | 200 到 230 | °C | |
| 加工（熔体）温度 | 200 到 230 | °C | |
| 模具温度 | 40.0 到 60.0 | °C | |
| 背压 | 0.490 到 0.981 | MPa | |
| 螺杆转速 | 30 到 60 | rpm |
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | 4.6kg |
| 7 . | 18.6kg |
| 8 . | 速率 A (50°C/h), 载荷2 (50N) |